MakeItFrom.com
Menu (ESC)

EQ21A Magnesium vs. Solder Alloy 712

EQ21A magnesium belongs to the magnesium alloys classification, while solder alloy 712 belongs to the otherwise unclassified metals. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EQ21A magnesium and the bottom bar is solder alloy 712.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 44
51
Elongation at Break, % 2.4
22
Poisson's Ratio 0.29
0.36
Shear Modulus, GPa 17
19
Tensile Strength: Ultimate (UTS), MPa 250
51

Thermal Properties

Latent Heat of Fusion, J/g 340
62
Melting Completion (Liquidus), °C 640
220
Melting Onset (Solidus), °C 560
220
Specific Heat Capacity, J/kg-K 980
220
Thermal Conductivity, W/m-K 110
58
Thermal Expansion, µm/m-K 27
22

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 25
13
Electrical Conductivity: Equal Weight (Specific), % IACS 120
16

Otherwise Unclassified Properties

Density, g/cm3 1.9
7.4
Embodied Carbon, kg CO2/kg material 27
18
Embodied Energy, MJ/kg 210
300

Common Calculations

Stiffness to Weight: Axial, points 13
3.8
Stiffness to Weight: Bending, points 63
17
Strength to Weight: Axial, points 37
1.9
Strength to Weight: Bending, points 47
4.1
Thermal Diffusivity, mm2/s 62
35
Thermal Shock Resistance, points 15
3.3

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.1
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Copper (Cu), % 0.050 to 0.1
0.5 to 0.9
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0
0 to 0.020
Lead (Pb), % 0
0 to 0.070
Magnesium (Mg), % 93.9 to 96.8
0
Nickel (Ni), % 0 to 0.010
0 to 0.010
Silver (Ag), % 1.3 to 1.7
3.3 to 3.7
Tin (Sn), % 0
94.9 to 96.2
Unspecified Rare Earths, % 1.5 to 3.0
0
Zinc (Zn), % 0
0 to 0.0010
Zirconium (Zr), % 0.4 to 1.0
0
Residuals, % 0 to 0.3
0