EV31A Magnesium vs. 7022 Aluminum
EV31A magnesium belongs to the magnesium alloys classification, while 7022 aluminum belongs to the aluminum alloys. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is EV31A magnesium and the bottom bar is 7022 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 44 | |
| 70 |
| Elongation at Break, % | 3.5 | |
| 6.3 to 8.0 |
| Fatigue Strength, MPa | 120 | |
| 140 to 170 |
| Poisson's Ratio | 0.27 | |
| 0.32 |
| Shear Modulus, GPa | 17 | |
| 26 |
| Shear Strength, MPa | 170 | |
| 290 to 320 |
| Tensile Strength: Ultimate (UTS), MPa | 260 | |
| 490 to 540 |
| Tensile Strength: Yield (Proof), MPa | 170 | |
| 390 to 460 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 200 | |
| 200 |
| Melting Onset (Solidus), °C | 590 | |
| 480 |
| Specific Heat Capacity, J/kg-K | 1000 | |
| 870 |
| Thermal Conductivity, W/m-K | 86 | |
| 140 |
| Thermal Expansion, µm/m-K | 27 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 18 | |
| 21 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 90 | |
| 65 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.8 | |
| 2.9 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 8.1 | |
| 29 to 40 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 330 | |
| 1100 to 1500 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 65 | |
| 47 |
| Strength to Weight: Axial, points | 40 | |
| 47 to 51 |
| Strength to Weight: Bending, points | 50 | |
| 47 to 50 |
| Thermal Diffusivity, mm2/s | 47 | |
| 54 |
| Thermal Shock Resistance, points | 16 | |
| 21 to 23 |