EV31A Magnesium vs. A206.0 Aluminum
EV31A magnesium belongs to the magnesium alloys classification, while A206.0 aluminum belongs to the aluminum alloys. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is EV31A magnesium and the bottom bar is A206.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 70 | |
| 100 to 110 |
| Elastic (Young's, Tensile) Modulus, GPa | 44 | |
| 70 |
| Elongation at Break, % | 3.5 | |
| 4.2 to 10 |
| Fatigue Strength, MPa | 120 | |
| 90 to 180 |
| Poisson's Ratio | 0.27 | |
| 0.33 |
| Shear Modulus, GPa | 17 | |
| 26 |
| Shear Strength, MPa | 170 | |
| 260 |
| Tensile Strength: Ultimate (UTS), MPa | 260 | |
| 390 to 440 |
| Tensile Strength: Yield (Proof), MPa | 170 | |
| 250 to 380 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 200 | |
| 170 |
| Melting Onset (Solidus), °C | 590 | |
| 550 |
| Specific Heat Capacity, J/kg-K | 1000 | |
| 880 |
| Thermal Conductivity, W/m-K | 86 | |
| 130 |
| Thermal Expansion, µm/m-K | 27 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 18 | |
| 30 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 90 | |
| 90 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.8 | |
| 3.0 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 8.1 | |
| 16 to 37 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 330 | |
| 440 to 1000 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 65 | |
| 46 |
| Strength to Weight: Axial, points | 40 | |
| 36 to 41 |
| Strength to Weight: Bending, points | 50 | |
| 39 to 43 |
| Thermal Diffusivity, mm2/s | 47 | |
| 48 |
| Thermal Shock Resistance, points | 16 | |
| 17 to 19 |