EV31A Magnesium vs. EN 1.0213 Steel
EV31A magnesium belongs to the magnesium alloys classification, while EN 1.0213 steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is EV31A magnesium and the bottom bar is EN 1.0213 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 70 | |
| 92 to 120 |
| Elastic (Young's, Tensile) Modulus, GPa | 44 | |
| 190 |
| Elongation at Break, % | 3.5 | |
| 12 to 25 |
| Fatigue Strength, MPa | 120 | |
| 160 to 240 |
| Poisson's Ratio | 0.27 | |
| 0.29 |
| Shear Modulus, GPa | 17 | |
| 73 |
| Shear Strength, MPa | 170 | |
| 230 to 270 |
| Tensile Strength: Ultimate (UTS), MPa | 260 | |
| 320 to 430 |
| Tensile Strength: Yield (Proof), MPa | 170 | |
| 220 to 330 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 200 | |
| 400 |
| Melting Onset (Solidus), °C | 590 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 1000 | |
| 470 |
| Thermal Conductivity, W/m-K | 86 | |
| 53 |
| Thermal Expansion, µm/m-K | 27 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 18 | |
| 6.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 90 | |
| 7.9 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.8 | |
| 7.9 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 8.1 | |
| 33 to 98 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 330 | |
| 120 to 300 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 65 | |
| 24 |
| Strength to Weight: Axial, points | 40 | |
| 11 to 15 |
| Strength to Weight: Bending, points | 50 | |
| 13 to 16 |
| Thermal Diffusivity, mm2/s | 47 | |
| 14 |
| Thermal Shock Resistance, points | 16 | |
| 10 to 14 |