EV31A Magnesium vs. EN 1.4612 Stainless Steel
EV31A magnesium belongs to the magnesium alloys classification, while EN 1.4612 stainless steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is EV31A magnesium and the bottom bar is EN 1.4612 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 44 | |
| 190 |
| Elongation at Break, % | 3.5 | |
| 11 |
| Fatigue Strength, MPa | 120 | |
| 860 to 950 |
| Poisson's Ratio | 0.27 | |
| 0.28 |
| Shear Modulus, GPa | 17 | |
| 76 |
| Shear Strength, MPa | 170 | |
| 1010 to 1110 |
| Tensile Strength: Ultimate (UTS), MPa | 260 | |
| 1690 to 1850 |
| Tensile Strength: Yield (Proof), MPa | 170 | |
| 1570 to 1730 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 200 | |
| 790 |
| Melting Onset (Solidus), °C | 590 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 1000 | |
| 480 |
| Thermal Expansion, µm/m-K | 27 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.8 | |
| 7.9 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 8.1 | |
| 190 to 210 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 65 | |
| 25 |
| Strength to Weight: Axial, points | 40 | |
| 60 to 65 |
| Strength to Weight: Bending, points | 50 | |
| 40 to 43 |
| Thermal Shock Resistance, points | 16 | |
| 58 to 63 |