EZ33A Magnesium vs. Grade 28 Titanium
EZ33A magnesium belongs to the magnesium alloys classification, while grade 28 titanium belongs to the titanium alloys. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is EZ33A magnesium and the bottom bar is grade 28 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 44 | |
| 110 |
| Elongation at Break, % | 2.6 | |
| 11 to 17 |
| Fatigue Strength, MPa | 70 | |
| 330 to 480 |
| Poisson's Ratio | 0.29 | |
| 0.32 |
| Shear Modulus, GPa | 17 | |
| 40 |
| Shear Strength, MPa | 140 | |
| 420 to 590 |
| Tensile Strength: Ultimate (UTS), MPa | 150 | |
| 690 to 980 |
| Tensile Strength: Yield (Proof), MPa | 100 | |
| 540 to 810 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 250 | |
| 330 |
| Melting Completion (Liquidus), °C | 640 | |
| 1640 |
| Melting Onset (Solidus), °C | 570 | |
| 1590 |
| Specific Heat Capacity, J/kg-K | 970 | |
| 550 |
| Thermal Conductivity, W/m-K | 100 | |
| 8.3 |
| Thermal Expansion, µm/m-K | 27 | |
| 9.9 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 24 | |
| 1.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 110 | |
| 2.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 25 | |
| 36 |
| Density, g/cm3 | 1.9 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 25 | |
| 37 |
| Embodied Energy, MJ/kg | 190 | |
| 600 |
| Embodied Water, L/kg | 930 | |
| 370 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 3.6 | |
| 87 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 | |
| 1370 to 3100 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 61 | |
| 35 |
| Strength to Weight: Axial, points | 22 | |
| 43 to 61 |
| Strength to Weight: Bending, points | 33 | |
| 39 to 49 |
| Thermal Diffusivity, mm2/s | 54 | |
| 3.4 |
| Thermal Shock Resistance, points | 9.2 | |
| 47 to 66 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 2.5 to 3.5 |
| Carbon (C), % | 0 | |
| 0 to 0.080 |
| Copper (Cu), % | 0 to 0.1 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 | |
| 0 to 0.25 |
| Magnesium (Mg), % | 91.5 to 95 | |
| 0 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.15 |
| Ruthenium (Ru), % | 0 | |
| 0.080 to 0.14 |
| Titanium (Ti), % | 0 | |
| 92.4 to 95.4 |
| Unspecified Rare Earths, % | 2.5 to 4.0 | |
| 0 |
| Vanadium (V), % | 0 | |
| 2.0 to 3.0 |
| Zinc (Zn), % | 2.0 to 3.1 | |
| 0 |
| Zirconium (Zr), % | 0.5 to 1.0 | |
| 0 |
| Residuals, % | 0 to 0.3 | |
| 0 to 0.4 |