EVA vs. POM-C
Both EVA and POM-C are thermoplastics. There are 9 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is EVA and the bottom bar is POM-C.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 0.93 to 1.0 | |
| 1.4 to 1.6 |
| Elastic (Young's, Tensile) Modulus, GPa | 0.015 to 0.080 | |
| 2.8 to 9.7 |
| Elongation at Break, % | 300 to 800 | |
| 3.0 to 65 |
| Specific Heat Capacity, J/kg-K | 1400 | |
| 1130 to 1370 |
| Stiffness to Weight: Axial, points | 0.0087 to 0.048 | |
| 1.1 to 3.3 |
| Stiffness to Weight: Bending, points | 8.6 to 15 | |
| 33 to 44 |
| Strength to Weight: Axial, points | 0.87 to 10 | |
| 12 to 19 |
| Strength to Weight: Bending, points | 4.8 to 26 | |
| 24 to 32 |
| Tensile Strength: Ultimate (UTS), MPa | 3.0 to 35 | |
| 61 to 110 |