EVA vs. PLA
Both EVA and PLA are thermoplastics. There are 12 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is EVA and the bottom bar is PLA.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 0.015 to 0.080 | |
| 3.5 |
| Elongation at Break, % | 300 to 800 | |
| 6.0 |
| Tensile Strength: Ultimate (UTS), MPa | 3.0 to 35 | |
| 50 |
Thermal Properties
| Melting Onset (Solidus), °C | 55 to 95 | |
| 160 |
| Specific Heat Capacity, J/kg-K | 1400 | |
| 1800 |
| Thermal Conductivity, W/m-K | 0.34 | |
| 0.13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 0.93 to 1.0 | |
| 1.3 |
Common Calculations
| Stiffness to Weight: Axial, points | 0.0087 to 0.048 | |
| 1.6 |
| Stiffness to Weight: Bending, points | 8.6 to 15 | |
| 40 |
| Strength to Weight: Axial, points | 0.87 to 10 | |
| 11 |
| Strength to Weight: Bending, points | 4.8 to 26 | |
| 24 |
| Thermal Diffusivity, mm2/s | 0.25 to 0.26 | |
| 0.058 |