H06 C66900 Brass vs. H06 C74500 Nickel Silver
Both H06 C66900 brass and H06 C74500 nickel silver are copper alloys. Both are furnished in the H06 (extra hard) temper. They have 88% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is H06 C66900 brass and the bottom bar is H06 C74500 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 120 |
| Elongation at Break, % | 3.0 | |
| 3.0 |
| Poisson's Ratio | 0.32 | |
| 0.32 |
| Rockwell B Hardness | 90 | |
| 92 |
| Rockwell Superficial 30T Hardness | 78 | |
| 78 |
| Shear Modulus, GPa | 45 | |
| 44 |
| Shear Strength, MPa | 380 | |
| 380 |
| Tensile Strength: Ultimate (UTS), MPa | 660 | |
| 660 |
| Tensile Strength: Yield (Proof), MPa | 660 | |
| 600 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 150 | |
| 170 |
| Melting Completion (Liquidus), °C | 860 | |
| 1020 |
| Melting Onset (Solidus), °C | 850 | |
| 970 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 390 |
| Thermal Expansion, µm/m-K | 20 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.4 | |
| 9.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.8 | |
| 9.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 29 |
| Density, g/cm3 | 8.2 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 3.4 |
| Embodied Energy, MJ/kg | 46 | |
| 54 |
| Embodied Water, L/kg | 310 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 20 | |
| 19 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1810 | |
| 1540 |
| Stiffness to Weight: Axial, points | 8.1 | |
| 7.7 |
| Stiffness to Weight: Bending, points | 20 | |
| 19 |
| Strength to Weight: Axial, points | 22 | |
| 22 |
| Strength to Weight: Bending, points | 21 | |
| 20 |
| Thermal Shock Resistance, points | 20 | |
| 22 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 62.5 to 64.5 | |
| 63.5 to 66.5 |
| Iron (Fe), % | 0 to 0.25 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 0.1 |
| Manganese (Mn), % | 11.5 to 12.5 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 | |
| 9.0 to 11 |
| Zinc (Zn), % | 22.5 to 26 | |
| 21.2 to 27.5 |
| Residuals, % | 0 to 0.2 | |
| 0 to 0.5 |