H06 C70600 Copper-nickel vs. H06 C72500 Copper-nickel
Both H06 C70600 copper-nickel and H06 C72500 copper-nickel are copper alloys. Both are furnished in the H06 (extra hard) temper. They have a very high 98% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is H06 C70600 copper-nickel and the bottom bar is H06 C72500 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 120 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Rockwell B Hardness | 83 | |
| 88 |
| Rockwell Superficial 30T Hardness | 74 | |
| 75 |
| Shear Modulus, GPa | 46 | |
| 45 |
| Tensile Strength: Ultimate (UTS), MPa | 540 | |
| 600 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 220 | |
| 210 |
| Melting Completion (Liquidus), °C | 1150 | |
| 1130 |
| Melting Onset (Solidus), °C | 1100 | |
| 1060 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 44 | |
| 54 |
| Thermal Expansion, µm/m-K | 17 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.8 | |
| 11 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.9 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 35 |
| Density, g/cm3 | 8.9 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 3.6 |
| Embodied Energy, MJ/kg | 51 | |
| 55 |
| Embodied Water, L/kg | 300 | |
| 320 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.7 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 17 | |
| 19 |
| Strength to Weight: Bending, points | 17 | |
| 18 |
| Thermal Diffusivity, mm2/s | 13 | |
| 16 |
| Thermal Shock Resistance, points | 18 | |
| 21 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 84.7 to 90 | |
| 85.2 to 89.7 |
| Iron (Fe), % | 1.0 to 1.8 | |
| 0 to 0.6 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 0.2 |
| Nickel (Ni), % | 9.0 to 11 | |
| 8.5 to 10.5 |
| Tin (Sn), % | 0 | |
| 1.8 to 2.8 |
| Zinc (Zn), % | 0 to 1.0 | |
| 0 to 0.5 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.2 |