H10 C34000 Brass vs. H10 C72500 Copper-nickel
Both H10 C34000 brass and H10 C72500 copper-nickel are copper alloys. Both are furnished in the H10 (extra spring) temper. They have 64% of their average alloy composition in common.
For each property being compared, the top bar is H10 C34000 brass and the bottom bar is H10 C72500 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 120 |
| Poisson's Ratio | 0.31 | |
| 0.34 |
| Rockwell B Hardness | 91 | |
| 91 |
| Rockwell Superficial 30T Hardness | 78 | |
| 78 |
| Shear Modulus, GPa | 40 | |
| 45 |
| Tensile Strength: Ultimate (UTS), MPa | 650 | |
| 670 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 210 |
| Melting Completion (Liquidus), °C | 930 | |
| 1130 |
| Melting Onset (Solidus), °C | 890 | |
| 1060 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 390 |
| Thermal Conductivity, W/m-K | 120 | |
| 54 |
| Thermal Expansion, µm/m-K | 21 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 26 | |
| 11 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 29 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 24 | |
| 35 |
| Density, g/cm3 | 8.1 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 3.6 |
| Embodied Energy, MJ/kg | 45 | |
| 55 |
| Embodied Water, L/kg | 320 | |
| 320 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.1 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 22 | |
| 21 |
| Strength to Weight: Bending, points | 21 | |
| 19 |
| Thermal Diffusivity, mm2/s | 37 | |
| 16 |
| Thermal Shock Resistance, points | 22 | |
| 23 |
Alloy Composition
| Copper (Cu), % | 62 to 65 | |
| 85.2 to 89.7 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.6 |
| Lead (Pb), % | 0.8 to 1.5 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 | |
| 0 to 0.2 |
| Nickel (Ni), % | 0 | |
| 8.5 to 10.5 |
| Tin (Sn), % | 0 | |
| 1.8 to 2.8 |
| Zinc (Zn), % | 33 to 37.2 | |
| 0 to 0.5 |
| Residuals, % | 0 | |
| 0 to 0.2 |