Full-hard K93600 vs. Full-hard N08800 Stainless Steel
Both full-hard K93600 and full-hard N08800 stainless steel are iron alloys. Both are furnished in the full-hard temper. There are 20 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is full-hard K93600 and the bottom bar is full-hard N08800 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 200 |
| Tensile Strength: Ultimate (UTS), MPa | 810 | |
| 1000 |
| Tensile Strength: Yield (Proof), MPa | 750 | |
| 830 |
Thermal Properties
| Curie Temperature, °C | 250 | |
| -120 |
| Maximum Temperature: Mechanical, °C | 440 | |
| 1100 |
| Melting Onset (Solidus), °C | 1430 | |
| 1360 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 480 |
| Thermal Conductivity, W/m-K | 13 | |
| 12 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 1.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
| 1.9 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 8.0 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 280 | |
| 42 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2050 | |
| 1740 |
| Stiffness to Weight: Axial, points | 9.4 | |
| 14 |
| Stiffness to Weight: Bending, points | 21 | |
| 24 |
| Strength to Weight: Axial, points | 28 | |
| 35 |
| Strength to Weight: Bending, points | 24 | |
| 28 |
| Thermal Diffusivity, mm2/s | 3.1 | |
| 3.0 |
| Thermal Shock Resistance, points | 57 | |
| 25 |