Fused Silica vs. Machinable Glass-ceramic
Both fused silica and machinable glass-ceramic are glass and glass-ceramics. There are 22 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is fused silica and the bottom bar is machinable glass-ceramic.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 1100 | |
| 310 |
| Elastic (Young's, Tensile) Modulus, GPa | 73 | |
| 67 |
| Flexural Strength, MPa | 67 | |
| 96 |
| Knoop Hardness | 570 | |
| 250 |
| Poisson's Ratio | 0.17 | |
| 0.29 |
| Shear Modulus, GPa | 31 | |
| 26 |
| Tensile Strength: Ultimate (UTS), MPa | 50 | |
| 84 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 1080 | |
| 760 |
| Specific Heat Capacity, J/kg-K | 720 | |
| 790 |
| Thermal Conductivity, W/m-K | 1.4 | |
| 1.2 |
| Thermal Expansion, µm/m-K | 0.5 | |
| 21 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 MHz | 3.8 | |
| 6.4 |
| Dielectric Strength (Breakdown Potential), kV/mm | 30 | |
| 27 |
| Electrical Dissipation At 1 MHz | 0.00011 | |
| 0.0050 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 14 | |
| 14 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.2 | |
| 2.7 |
Common Calculations
| Stiffness to Weight: Axial, points | 18 | |
| 14 |
| Stiffness to Weight: Bending, points | 63 | |
| 51 |
| Strength to Weight: Axial, points | 6.3 | |
| 8.8 |
| Strength to Weight: Bending, points | 14 | |
| 16 |
| Thermal Diffusivity, mm2/s | 0.85 | |
| 0.56 |
| Thermal Shock Resistance, points | 97 | |
| 4.3 |