G-CoCr28 Cobalt vs. SAE-AISI 8645 Steel
G-CoCr28 cobalt belongs to the cobalt alloys classification, while SAE-AISI 8645 steel belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is G-CoCr28 cobalt and the bottom bar is SAE-AISI 8645 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Elongation at Break, % | 6.7 | |
| 12 to 23 |
| Fatigue Strength, MPa | 130 | |
| 280 to 350 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 83 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 560 | |
| 600 to 670 |
| Tensile Strength: Yield (Proof), MPa | 260 | |
| 390 to 560 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 1200 | |
| 410 |
| Melting Completion (Liquidus), °C | 1330 | |
| 1460 |
| Melting Onset (Solidus), °C | 1270 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 8.5 | |
| 39 |
| Thermal Expansion, µm/m-K | 14 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 100 | |
| 2.6 |
| Density, g/cm3 | 8.1 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 6.2 | |
| 1.5 |
| Embodied Energy, MJ/kg | 84 | |
| 20 |
| Embodied Water, L/kg | 440 | |
| 50 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 31 | |
| 77 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 160 | |
| 420 to 840 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 19 | |
| 21 to 24 |
| Strength to Weight: Bending, points | 19 | |
| 20 to 22 |
| Thermal Diffusivity, mm2/s | 2.2 | |
| 10 |
| Thermal Shock Resistance, points | 14 | |
| 18 to 20 |
Alloy Composition
| Carbon (C), % | 0.050 to 0.25 | |
| 0.43 to 0.48 |
| Chromium (Cr), % | 27 to 30 | |
| 0.4 to 0.6 |
| Cobalt (Co), % | 48 to 52 | |
| 0 |
| Iron (Fe), % | 9.7 to 24.5 | |
| 96.5 to 97.7 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0.75 to 1.0 |
| Molybdenum (Mo), % | 0 to 0.5 | |
| 0.15 to 0.25 |
| Nickel (Ni), % | 0 to 4.0 | |
| 0.4 to 0.7 |
| Niobium (Nb), % | 0 to 0.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.035 |
| Silicon (Si), % | 0.5 to 1.5 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.040 |