PETG vs. HIPS
Both PETG and HIPS are thermoplastics. There are 17 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.
For each property being compared, the top bar is PETG and the bottom bar is HIPS.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 2.2 | |
| 1.9 |
| Flexural Strength, MPa | 77 | |
| 62 |
| Impact Strength: Notched Izod, J/m | 77 | |
| 45 |
| Tensile Strength: Ultimate (UTS), MPa | 53 | |
| 32 |
Thermal Properties
| Glass Transition Temperature, °C | 81 | |
| 100 |
| Specific Heat Capacity, J/kg-K | 1200 | |
| 1400 |
| Thermal Conductivity, W/m-K | 0.29 | |
| 0.22 |
| Thermal Expansion, µm/m-K | 68 | |
| 80 |
Electrical Properties
| Dielectric Strength (Breakdown Potential), kV/mm | 16 | |
| 18 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.3 | |
| 1.0 |
| Water Absorption After 24 Hours, % | 0.2 | |
| 0.080 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.0 | |
| 1.0 |
| Stiffness to Weight: Bending, points | 34 | |
| 40 |
| Strength to Weight: Axial, points | 12 | |
| 8.5 |
| Strength to Weight: Bending, points | 25 | |
| 22 |
| Thermal Diffusivity, mm2/s | 0.19 | |
| 0.15 |
| Thermal Shock Resistance, points | 25 | |
| 15 |