PETG vs. PA 6/10
Both PETG and PA 6/10 are thermoplastics. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is PETG and the bottom bar is PA 6/10.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 2.2 | |
| 1.6 to 2.3 |
| Flexural Modulus, GPa | 2.1 | |
| 1.4 to 2.0 |
| Flexural Strength, MPa | 77 | |
| 48 to 59 |
| Impact Strength: Notched Izod, J/m | 77 | |
| 85 |
| Tensile Strength: Ultimate (UTS), MPa | 53 | |
| 45 to 60 |
Thermal Properties
| Melting Onset (Solidus), °C | 140 | |
| 220 |
| Specific Heat Capacity, J/kg-K | 1200 | |
| 1510 |
| Thermal Conductivity, W/m-K | 0.29 | |
| 0.23 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 Hz | 2.6 | |
| 3.9 to 12 |
| Dielectric Strength (Breakdown Potential), kV/mm | 16 | |
| 15 to 19 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.3 | |
| 1.1 |
| Water Absorption After 24 Hours, % | 0.2 | |
| 0.26 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.0 | |
| 0.78 to 1.1 |
| Stiffness to Weight: Bending, points | 34 | |
| 34 to 39 |
| Strength to Weight: Axial, points | 12 | |
| 11 to 15 |
| Strength to Weight: Bending, points | 25 | |
| 25 to 30 |
| Thermal Diffusivity, mm2/s | 0.19 | |
| 0.13 |