PETG vs. PA 6/6
Both PETG and PA 6/6 are thermoplastics. There are 9 material properties with values for both materials. Properties with values for just one material (23, in this case) are not shown.
For each property being compared, the top bar is PETG and the bottom bar is PA 6/6.
Metric UnitsUS Customary Units
Material Properties
| Dielectric Constant (Relative Permittivity) At 1 Hz | 2.6 | |
| 3.6 to 15 |
| Dielectric Constant (Relative Permittivity) At 1 MHz | 2.4 | |
| 3.0 to 4.3 |
| Dielectric Strength (Breakdown Potential), kV/mm | 16 | |
| 25 to 30 |
| Elastic (Young's, Tensile) Modulus, GPa | 2.2 | |
| 1.6 to 23 |
| Flexural Modulus, GPa | 2.1 | |
| 1.3 to 19 |
| Flexural Strength, MPa | 77 | |
| 80 to 260 |
| Glass Transition Temperature, °C | 81 | |
| 50 |
| Melting Onset (Solidus), °C | 140 | |
| 260 |
| Tensile Strength: Ultimate (UTS), MPa | 53 | |
| 60 to 240 |