PETG vs. Unfilled Thermoplastic PI
Both PETG and unfilled thermoplastic PI are thermoplastics. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is PETG and the bottom bar is unfilled thermoplastic PI.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 55 | |
| 240 |
| Elastic (Young's, Tensile) Modulus, GPa | 2.2 | |
| 3.7 |
| Flexural Modulus, GPa | 2.1 | |
| 3.8 |
| Flexural Strength, MPa | 77 | |
| 170 |
| Impact Strength: Notched Izod, J/m | 77 | |
| 83 |
| Shear Strength, MPa | 62 | |
| 110 |
| Tensile Strength: Ultimate (UTS), MPa | 53 | |
| 110 |
Thermal Properties
| Glass Transition Temperature, °C | 81 | |
| 260 |
| Heat Deflection Temperature At 1.82 MPa (264 psi), °C | 69 | |
| 340 |
| Specific Heat Capacity, J/kg-K | 1200 | |
| 1100 |
| Thermal Conductivity, W/m-K | 0.29 | |
| 0.11 |
| Thermal Expansion, µm/m-K | 68 | |
| 45 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 MHz | 2.4 | |
| 3.2 |
| Dielectric Strength (Breakdown Potential), kV/mm | 16 | |
| 16 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.3 | |
| 1.4 |
| Water Absorption After 24 Hours, % | 0.2 | |
| 0.7 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.0 | |
| 1.5 |
| Stiffness to Weight: Bending, points | 34 | |
| 37 |
| Strength to Weight: Axial, points | 12 | |
| 22 |
| Strength to Weight: Bending, points | 25 | |
| 36 |
| Thermal Diffusivity, mm2/s | 0.19 | |
| 0.072 |
| Thermal Shock Resistance, points | 25 | |
| 46 |