Grade 1 Babbitt Metal vs. ASTM B628 Ag-Cu
Both grade 1 Babbitt Metal and ASTM B628 Ag-Cu are otherwise unclassified metals. There are 14 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is grade 1 Babbitt Metal and the bottom bar is ASTM B628 Ag-Cu.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 53 | |
| 83 |
| Elongation at Break, % | 34 | |
| 1.1 to 17 |
| Poisson's Ratio | 0.35 | |
| 0.36 |
| Shear Modulus, GPa | 20 | |
| 31 |
Thermal Properties
| Latent Heat of Fusion, J/g | 70 | |
| 140 |
| Melting Completion (Liquidus), °C | 370 | |
| 780 |
| Melting Onset (Solidus), °C | 220 | |
| 780 |
| Specific Heat Capacity, J/kg-K | 230 | |
| 280 |
| Thermal Expansion, µm/m-K | 21 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 13 | |
| 84 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 16 | |
| 75 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.3 | |
| 10 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.0 | |
| 4.6 |
| Stiffness to Weight: Bending, points | 17 | |
| 14 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 to 0.0050 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 4.0 to 5.0 | |
| 0 |
| Arsenic (As), % | 0 to 0.1 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.080 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.050 | |
| 0 to 0.050 |
| Copper (Cu), % | 4.0 to 5.0 | |
| 26.6 to 29 |
| Iron (Fe), % | 0 to 0.080 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 to 0.35 | |
| 0 to 0.030 |
| Nickel (Ni), % | 0 | |
| 0 to 0.010 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silver (Ag), % | 0 | |
| 71 to 73 |
| Tin (Sn), % | 89.3 to 92 | |
| 0 |
| Zinc (Zn), % | 0 to 0.0050 | |
| 0 to 0.060 |
| Residuals, % | 0 | |
| 0 to 0.21 |