Grade 1 Babbitt Metal vs. Austempered Cast Iron
Grade 1 Babbitt Metal belongs to the otherwise unclassified metals classification, while austempered cast iron belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is grade 1 Babbitt Metal and the bottom bar is austempered cast iron.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 13 | |
| 270 to 490 |
| Elastic (Young's, Tensile) Modulus, GPa | 53 | |
| 180 |
| Elongation at Break, % | 34 | |
| 1.1 to 13 |
| Poisson's Ratio | 0.35 | |
| 0.29 |
| Shear Modulus, GPa | 20 | |
| 62 to 69 |
| Tensile Strength: Yield (Proof), MPa | 30 | |
| 560 to 1460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 70 | |
| 280 |
| Melting Completion (Liquidus), °C | 370 | |
| 1380 |
| Melting Onset (Solidus), °C | 220 | |
| 1340 |
| Specific Heat Capacity, J/kg-K | 230 | |
| 490 |
| Thermal Conductivity, W/m-K | 45 | |
| 42 |
| Thermal Expansion, µm/m-K | 21 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 75 | |
| 2.9 |
| Density, g/cm3 | 7.3 | |
| 7.5 |
| Embodied Carbon, kg CO2/kg material | 12 | |
| 1.8 |
| Embodied Energy, MJ/kg | 200 | |
| 25 |
| Embodied Water, L/kg | 1160 | |
| 48 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 8.6 | |
| 880 to 3970 |
| Stiffness to Weight: Axial, points | 4.0 | |
| 13 |
| Stiffness to Weight: Bending, points | 17 | |
| 25 |
| Thermal Diffusivity, mm2/s | 26 | |
| 11 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0050 | |
| 0 to 0.050 |
| Antimony (Sb), % | 4.0 to 5.0 | |
| 0 |
| Arsenic (As), % | 0 to 0.1 | |
| 0 to 0.020 |
| Bismuth (Bi), % | 0 to 0.080 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.050 | |
| 0 |
| Carbon (C), % | 0 | |
| 3.4 to 3.8 |
| Chromium (Cr), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 4.0 to 5.0 | |
| 0 to 0.8 |
| Iron (Fe), % | 0 to 0.080 | |
| 89.6 to 94 |
| Lead (Pb), % | 0 to 0.35 | |
| 0 |
| Magnesium (Mg), % | 0 | |
| 0 to 0.040 |
| Manganese (Mn), % | 0 | |
| 0.3 to 0.4 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.3 |
| Nickel (Ni), % | 0 | |
| 0 to 2.0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Selenium (Se), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 2.3 to 2.7 |
| Sulfur (S), % | 0 | |
| 0 to 0.020 |
| Tin (Sn), % | 89.3 to 92 | |
| 0 to 0.020 |
| Vanadium (V), % | 0 | |
| 0 to 0.1 |
| Zinc (Zn), % | 0 to 0.0050 | |
| 0 |