Grade 1 Babbitt Metal vs. C76200 Nickel Silver
Grade 1 Babbitt Metal belongs to the otherwise unclassified metals classification, while C76200 nickel silver belongs to the copper alloys. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is grade 1 Babbitt Metal and the bottom bar is C76200 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 53 | |
| 120 |
| Poisson's Ratio | 0.35 | |
| 0.31 |
| Shear Modulus, GPa | 20 | |
| 44 |
Thermal Properties
| Latent Heat of Fusion, J/g | 70 | |
| 190 |
| Melting Completion (Liquidus), °C | 370 | |
| 1030 |
| Melting Onset (Solidus), °C | 220 | |
| 980 |
| Specific Heat Capacity, J/kg-K | 230 | |
| 390 |
| Thermal Conductivity, W/m-K | 45 | |
| 45 |
| Thermal Expansion, µm/m-K | 21 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 13 | |
| 9.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 16 | |
| 9.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 75 | |
| 29 |
| Density, g/cm3 | 7.3 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 12 | |
| 3.6 |
| Embodied Energy, MJ/kg | 200 | |
| 57 |
| Embodied Water, L/kg | 1160 | |
| 310 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.0 | |
| 7.8 |
| Stiffness to Weight: Bending, points | 17 | |
| 20 |
| Thermal Diffusivity, mm2/s | 26 | |
| 14 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 to 0.0050 | |
| 0 |
| Antimony (Sb), % | 4.0 to 5.0 | |
| 0 |
| Arsenic (As), % | 0 to 0.1 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.080 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.050 | |
| 0 |
| Copper (Cu), % | 4.0 to 5.0 | |
| 57 to 61 |
| Iron (Fe), % | 0 to 0.080 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 to 0.35 | |
| 0 to 0.1 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 | |
| 11 to 13.5 |
| Tin (Sn), % | 89.3 to 92 | |
| 0 |
| Zinc (Zn), % | 0 to 0.0050 | |
| 24.2 to 32 |
| Residuals, % | 0 | |
| 0 to 0.5 |