Grade 11 Titanium vs. 5040 Aluminum
Grade 11 titanium belongs to the titanium alloys classification, while 5040 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is grade 11 titanium and the bottom bar is 5040 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 120 | |
| 66 to 74 |
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 70 |
| Elongation at Break, % | 29 | |
| 5.7 to 6.8 |
| Fatigue Strength, MPa | 170 | |
| 100 to 130 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Shear Modulus, GPa | 38 | |
| 26 |
| Shear Strength, MPa | 200 | |
| 140 to 150 |
| Tensile Strength: Ultimate (UTS), MPa | 310 | |
| 240 to 260 |
| Tensile Strength: Yield (Proof), MPa | 230 | |
| 190 to 230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 420 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 320 | |
| 190 |
| Melting Completion (Liquidus), °C | 1660 | |
| 650 |
| Melting Onset (Solidus), °C | 1610 | |
| 600 |
| Specific Heat Capacity, J/kg-K | 540 | |
| 900 |
| Thermal Conductivity, W/m-K | 22 | |
| 160 |
| Thermal Expansion, µm/m-K | 9.2 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.7 | |
| 41 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.3 | |
| 130 |
Otherwise Unclassified Properties
| Density, g/cm3 | 4.5 | |
| 2.8 |
| Embodied Carbon, kg CO2/kg material | 47 | |
| 8.3 |
| Embodied Energy, MJ/kg | 800 | |
| 150 |
| Embodied Water, L/kg | 470 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 81 | |
| 14 to 15 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 240 | |
| 260 to 380 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 35 | |
| 50 |
| Strength to Weight: Axial, points | 19 | |
| 24 to 26 |
| Strength to Weight: Bending, points | 22 | |
| 31 to 32 |
| Thermal Diffusivity, mm2/s | 8.9 | |
| 64 |
| Thermal Shock Resistance, points | 22 | |
| 10 to 11 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 95.2 to 98 |
| Carbon (C), % | 0 to 0.080 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0.1 to 0.3 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.2 | |
| 0 to 0.7 |
| Magnesium (Mg), % | 0 | |
| 1.0 to 1.5 |
| Manganese (Mn), % | 0 | |
| 0.9 to 1.4 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.18 | |
| 0 |
| Palladium (Pd), % | 0.12 to 0.25 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.3 |
| Titanium (Ti), % | 98.8 to 99.88 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.25 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.15 |