Grade 11 Titanium vs. 7049A Aluminum
Grade 11 titanium belongs to the titanium alloys classification, while 7049A aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is grade 11 titanium and the bottom bar is 7049A aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 71 |
| Elongation at Break, % | 29 | |
| 5.0 to 5.7 |
| Fatigue Strength, MPa | 170 | |
| 180 |
| Poisson's Ratio | 0.32 | |
| 0.32 |
| Shear Modulus, GPa | 38 | |
| 27 |
| Shear Strength, MPa | 200 | |
| 340 to 350 |
| Tensile Strength: Ultimate (UTS), MPa | 310 | |
| 580 to 590 |
| Tensile Strength: Yield (Proof), MPa | 230 | |
| 500 to 530 |
Thermal Properties
| Latent Heat of Fusion, J/g | 420 | |
| 370 |
| Maximum Temperature: Mechanical, °C | 320 | |
| 200 |
| Melting Completion (Liquidus), °C | 1660 | |
| 640 |
| Melting Onset (Solidus), °C | 1610 | |
| 430 |
| Specific Heat Capacity, J/kg-K | 540 | |
| 850 |
| Thermal Conductivity, W/m-K | 22 | |
| 130 |
| Thermal Expansion, µm/m-K | 9.2 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.7 | |
| 40 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.3 | |
| 120 |
Otherwise Unclassified Properties
| Density, g/cm3 | 4.5 | |
| 3.1 |
| Embodied Carbon, kg CO2/kg material | 47 | |
| 8.2 |
| Embodied Energy, MJ/kg | 800 | |
| 150 |
| Embodied Water, L/kg | 470 | |
| 1100 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 81 | |
| 28 to 32 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 240 | |
| 1800 to 1990 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 35 | |
| 44 |
| Strength to Weight: Axial, points | 19 | |
| 52 to 53 |
| Strength to Weight: Bending, points | 22 | |
| 50 to 51 |
| Thermal Diffusivity, mm2/s | 8.9 | |
| 50 |
| Thermal Shock Resistance, points | 22 | |
| 25 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 84.6 to 89.5 |
| Carbon (C), % | 0 to 0.080 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0.050 to 0.25 |
| Copper (Cu), % | 0 | |
| 1.2 to 1.9 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.2 | |
| 0 to 0.5 |
| Magnesium (Mg), % | 0 | |
| 2.1 to 3.1 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.18 | |
| 0 |
| Palladium (Pd), % | 0.12 to 0.25 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.4 |
| Titanium (Ti), % | 98.8 to 99.88 | |
| 0 to 0.25 |
| Zinc (Zn), % | 0 | |
| 7.2 to 8.4 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.25 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.15 |