Grade 11 Titanium vs. Z13004 Zinc

Grade 11 titanium belongs to the titanium alloys classification, while Z13004 zinc belongs to the zinc alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is grade 11 titanium and the bottom bar is Z13004 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
87
Elongation at Break, % 29
30
Poisson's Ratio 0.32
0.25
Shear Modulus, GPa 38
35
Tensile Strength: Ultimate (UTS), MPa 310
93
Tensile Strength: Yield (Proof), MPa 230
76

Thermal Properties

Latent Heat of Fusion, J/g 420
110
Maximum Temperature: Mechanical, °C 320
90
Melting Completion (Liquidus), °C 1660
410
Melting Onset (Solidus), °C 1610
390
Specific Heat Capacity, J/kg-K 540
390
Thermal Conductivity, W/m-K 22
110
Thermal Expansion, µm/m-K 9.2
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.7
27
Electrical Conductivity: Equal Weight (Specific), % IACS 7.3
37

Otherwise Unclassified Properties

Density, g/cm3 4.5
6.6
Embodied Carbon, kg CO2/kg material 47
2.8
Embodied Energy, MJ/kg 800
53
Embodied Water, L/kg 470
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 81
26
Resilience: Unit (Modulus of Resilience), kJ/m3 240
33
Stiffness to Weight: Axial, points 13
7.4
Stiffness to Weight: Bending, points 35
23
Strength to Weight: Axial, points 19
3.9
Strength to Weight: Bending, points 22
7.0
Thermal Diffusivity, mm2/s 8.9
44
Thermal Shock Resistance, points 22
2.9

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0020
Cadmium (Cd), % 0
0 to 0.0030
Carbon (C), % 0 to 0.080
0
Copper (Cu), % 0
0 to 0.0030
Hydrogen (H), % 0 to 0.015
0
Iron (Fe), % 0 to 0.2
0 to 0.0030
Lead (Pb), % 0
0 to 0.0030
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.18
0
Palladium (Pd), % 0.12 to 0.25
0
Tin (Sn), % 0
0 to 0.0010
Titanium (Ti), % 98.8 to 99.88
0
Zinc (Zn), % 0
99.985 to 100
Residuals, % 0 to 0.4
0