Grade 11 Titanium vs. C71520 Copper-nickel
Grade 11 titanium belongs to the titanium alloys classification, while C71520 copper-nickel belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is grade 11 titanium and the bottom bar is C71520 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 140 |
| Elongation at Break, % | 29 | |
| 10 to 45 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Shear Modulus, GPa | 38 | |
| 51 |
| Shear Strength, MPa | 200 | |
| 250 to 340 |
| Tensile Strength: Ultimate (UTS), MPa | 310 | |
| 370 to 570 |
| Tensile Strength: Yield (Proof), MPa | 230 | |
| 140 to 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 420 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 320 | |
| 260 |
| Melting Completion (Liquidus), °C | 1660 | |
| 1170 |
| Melting Onset (Solidus), °C | 1610 | |
| 1120 |
| Specific Heat Capacity, J/kg-K | 540 | |
| 400 |
| Thermal Conductivity, W/m-K | 22 | |
| 32 |
| Thermal Expansion, µm/m-K | 9.2 | |
| 15 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.7 | |
| 5.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.3 | |
| 5.8 |
Otherwise Unclassified Properties
| Density, g/cm3 | 4.5 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 47 | |
| 5.0 |
| Embodied Energy, MJ/kg | 800 | |
| 73 |
| Embodied Water, L/kg | 470 | |
| 280 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 81 | |
| 54 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 240 | |
| 67 to 680 |
| Stiffness to Weight: Axial, points | 13 | |
| 8.6 |
| Stiffness to Weight: Bending, points | 35 | |
| 19 |
| Strength to Weight: Axial, points | 19 | |
| 12 to 18 |
| Strength to Weight: Bending, points | 22 | |
| 13 to 17 |
| Thermal Diffusivity, mm2/s | 8.9 | |
| 8.9 |
| Thermal Shock Resistance, points | 22 | |
| 12 to 19 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0 to 0.080 | |
| 0 to 0.050 |
| Copper (Cu), % | 0 | |
| 65 to 71.6 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.2 | |
| 0.4 to 1.0 |
| Lead (Pb), % | 0 | |
| 0 to 0.020 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0 | |
| 28 to 33 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.18 | |
| 0 |
| Palladium (Pd), % | 0.12 to 0.25 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.2 |
| Sulfur (S), % | 0 | |
| 0 to 0.020 |
| Titanium (Ti), % | 98.8 to 99.88 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.5 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.5 |