Grade 15 Babbitt Metal vs. ACI-ASTM CN7M Steel

Grade 15 Babbitt Metal belongs to the otherwise unclassified metals classification, while ACI-ASTM CN7M steel belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is grade 15 Babbitt Metal and the bottom bar is ACI-ASTM CN7M steel.

Grade 15 (L53620) Lead-Base Babbitt Metal ACI-ASTM CN7M (J95150) Cast Stainless Steel

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness		21
Brinell Hardness		140

Elastic (Young's, Tensile) Modulus, GPa		23
Elastic (Young's, Tensile) Modulus, GPa		200

Poisson's Ratio		0.4
Poisson's Ratio		0.28

Shear Modulus, GPa		8.2
Shear Modulus, GPa		77

Thermal Properties

Latent Heat of Fusion, J/g		46
Latent Heat of Fusion, J/g		310

Melting Completion (Liquidus), °C		280
Melting Completion (Liquidus), °C		1410

Melting Onset (Solidus), °C		250
Melting Onset (Solidus), °C		1450

Specific Heat Capacity, J/kg-K		140
Specific Heat Capacity, J/kg-K		470

Thermal Expansion, µm/m-K		26
Thermal Expansion, µm/m-K		15

Otherwise Unclassified Properties

Base Metal Price, % relative		17
Base Metal Price, % relative		32

Density, g/cm³		10
Density, g/cm³		8.1

Embodied Carbon, kg CO₂/kg material		3.6
Embodied Carbon, kg CO₂/kg material		5.6

Embodied Energy, MJ/kg		47
Embodied Energy, MJ/kg		78

Embodied Water, L/kg		840
Embodied Water, L/kg		210

Common Calculations

Stiffness to Weight: Axial, points		1.2
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		9.0
Stiffness to Weight: Bending, points		24

Alloy Composition

Aluminum (Al), %		0 to 0.0050
Aluminum (Al), %		0

Antimony (Sb), %		14.5 to 17.5
Antimony (Sb), %		0

Arsenic (As), %		0.8 to 1.4
Arsenic (As), %		0

Bismuth (Bi), %		0 to 0.1
Bismuth (Bi), %		0

Cadmium (Cd), %		0 to 0.050
Cadmium (Cd), %		0

Carbon (C), %		0
Carbon (C), %		0 to 0.070

Chromium (Cr), %		0
Chromium (Cr), %		19 to 22

Copper (Cu), %		0 to 0.6
Copper (Cu), %		3.0 to 4.0

Iron (Fe), %		0 to 0.1
Iron (Fe), %		37.4 to 48.5

Lead (Pb), %		79 to 83.9
Lead (Pb), %		0

Manganese (Mn), %		0
Manganese (Mn), %		0 to 1.5

Molybdenum (Mo), %		0
Molybdenum (Mo), %		2.0 to 3.0

Nickel (Ni), %		0
Nickel (Ni), %		27.5 to 30.5

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.040

Silicon (Si), %		0
Silicon (Si), %		0 to 1.5

Sulfur (S), %		0
Sulfur (S), %		0 to 0.040

Tin (Sn), %		0.8 to 1.2
Tin (Sn), %		0

Zinc (Zn), %		0 to 0.0050
Zinc (Zn), %		0