Grade 18 Titanium vs. EN 1.4029 Stainless Steel
Grade 18 titanium belongs to the titanium alloys classification, while EN 1.4029 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is grade 18 titanium and the bottom bar is EN 1.4029 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Elongation at Break, % | 11 to 17 | |
| 10 to 20 |
| Fatigue Strength, MPa | 330 to 480 | |
| 270 to 400 |
| Poisson's Ratio | 0.32 | |
| 0.28 |
| Shear Modulus, GPa | 40 | |
| 76 |
| Shear Strength, MPa | 420 to 590 | |
| 440 to 550 |
| Tensile Strength: Ultimate (UTS), MPa | 690 to 980 | |
| 700 to 930 |
| Tensile Strength: Yield (Proof), MPa | 540 to 810 | |
| 410 to 740 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 330 | |
| 750 |
| Melting Completion (Liquidus), °C | 1640 | |
| 1440 |
| Melting Onset (Solidus), °C | 1590 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 550 | |
| 480 |
| Thermal Conductivity, W/m-K | 8.3 | |
| 30 |
| Thermal Expansion, µm/m-K | 9.9 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.3 | |
| 3.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 3.7 |
Otherwise Unclassified Properties
| Density, g/cm3 | 4.5 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 41 | |
| 2.0 |
| Embodied Energy, MJ/kg | 670 | |
| 28 |
| Embodied Water, L/kg | 270 | |
| 100 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 87 to 110 | |
| 89 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1380 to 3110 | |
| 440 to 1410 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 35 | |
| 25 |
| Strength to Weight: Axial, points | 43 to 61 | |
| 25 to 33 |
| Strength to Weight: Bending, points | 39 to 49 | |
| 23 to 27 |
| Thermal Diffusivity, mm2/s | 3.4 | |
| 8.1 |
| Thermal Shock Resistance, points | 47 to 67 | |
| 26 to 34 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 2.5 to 3.5 | |
| 0 |
| Carbon (C), % | 0 to 0.080 | |
| 0.25 to 0.32 |
| Chromium (Cr), % | 0 | |
| 12 to 13.5 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.25 | |
| 82.8 to 87.6 |
| Manganese (Mn), % | 0 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.6 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.15 | |
| 0 |
| Palladium (Pd), % | 0.040 to 0.080 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0.15 to 0.25 |
| Titanium (Ti), % | 92.5 to 95.5 | |
| 0 |
| Vanadium (V), % | 2.0 to 3.0 | |
| 0 |
| Residuals, % | 0 to 0.4 | |
| 0 |