Grade 19 Titanium vs. R04295 Alloy
Grade 19 titanium belongs to the titanium alloys classification, while R04295 alloy belongs to the otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is grade 19 titanium and the bottom bar is R04295 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 100 |
| Elongation at Break, % | 5.6 to 17 | |
| 22 |
| Poisson's Ratio | 0.32 | |
| 0.38 |
| Shear Modulus, GPa | 47 | |
| 37 |
| Tensile Strength: Ultimate (UTS), MPa | 890 to 1300 | |
| 410 |
| Tensile Strength: Yield (Proof), MPa | 870 to 1170 | |
| 300 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 300 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 260 |
| Thermal Expansion, µm/m-K | 9.1 | |
| 7.2 |
Otherwise Unclassified Properties
| Density, g/cm3 | 5.0 | |
| 9.0 |
| Embodied Water, L/kg | 230 | |
| 950 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 70 to 150 | |
| 84 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 3040 to 5530 | |
| 430 |
| Stiffness to Weight: Axial, points | 14 | |
| 6.3 |
| Stiffness to Weight: Bending, points | 33 | |
| 17 |
| Strength to Weight: Axial, points | 49 to 72 | |
| 13 |
| Strength to Weight: Bending, points | 41 to 53 | |
| 14 |
| Thermal Shock Resistance, points | 57 to 83 | |
| 40 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 3.0 to 4.0 | |
| 0 |
| Carbon (C), % | 0 to 0.050 | |
| 0 to 0.015 |
| Chromium (Cr), % | 5.5 to 6.5 | |
| 0 |
| Hafnium (Hf), % | 0 | |
| 9.0 to 11 |
| Hydrogen (H), % | 0 to 0.020 | |
| 0 to 0.0015 |
| Iron (Fe), % | 0 to 0.3 | |
| 0 |
| Molybdenum (Mo), % | 3.5 to 4.5 | |
| 0 |
| Niobium (Nb), % | 0 | |
| 85.9 to 90.3 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 to 0.010 |
| Oxygen (O), % | 0 to 0.12 | |
| 0 to 0.025 |
| Tantalum (Ta), % | 0 | |
| 0 to 0.5 |
| Titanium (Ti), % | 71.1 to 77 | |
| 0.7 to 1.3 |
| Tungsten (W), % | 0 | |
| 0 to 0.5 |
| Vanadium (V), % | 7.5 to 8.5 | |
| 0 |
| Zirconium (Zr), % | 3.5 to 4.5 | |
| 0 to 0.7 |
| Residuals, % | 0 to 0.4 | |
| 0 |