Grade 20 Titanium vs. C33000 Brass
Grade 20 titanium belongs to the titanium alloys classification, while C33000 brass belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is grade 20 titanium and the bottom bar is C33000 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Elongation at Break, % | 5.7 to 17 | |
| 7.0 to 60 |
| Poisson's Ratio | 0.32 | |
| 0.31 |
| Shear Modulus, GPa | 47 | |
| 40 |
| Shear Strength, MPa | 560 to 740 | |
| 240 to 300 |
| Tensile Strength: Ultimate (UTS), MPa | 900 to 1270 | |
| 320 to 520 |
| Tensile Strength: Yield (Proof), MPa | 850 to 1190 | |
| 110 to 450 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 180 |
| Maximum Temperature: Mechanical, °C | 370 | |
| 130 |
| Melting Completion (Liquidus), °C | 1660 | |
| 940 |
| Melting Onset (Solidus), °C | 1600 | |
| 900 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 390 |
| Thermal Expansion, µm/m-K | 9.6 | |
| 20 |
Otherwise Unclassified Properties
| Density, g/cm3 | 5.0 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 52 | |
| 2.7 |
| Embodied Energy, MJ/kg | 860 | |
| 45 |
| Embodied Water, L/kg | 350 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 71 to 150 | |
| 35 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2940 to 5760 | |
| 60 to 950 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 33 | |
| 19 |
| Strength to Weight: Axial, points | 50 to 70 | |
| 11 to 18 |
| Strength to Weight: Bending, points | 41 to 52 | |
| 13 to 18 |
| Thermal Shock Resistance, points | 55 to 77 | |
| 11 to 17 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 3.0 to 4.0 | |
| 0 |
| Carbon (C), % | 0 to 0.050 | |
| 0 |
| Chromium (Cr), % | 5.5 to 6.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 65 to 68 |
| Hydrogen (H), % | 0 to 0.020 | |
| 0 |
| Iron (Fe), % | 0 to 0.3 | |
| 0 to 0.070 |
| Lead (Pb), % | 0 | |
| 0.25 to 0.7 |
| Molybdenum (Mo), % | 3.5 to 4.5 | |
| 0 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.12 | |
| 0 |
| Palladium (Pd), % | 0.040 to 0.080 | |
| 0 |
| Titanium (Ti), % | 71 to 77 | |
| 0 |
| Vanadium (V), % | 7.5 to 8.5 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 30.8 to 34.8 |
| Zirconium (Zr), % | 3.5 to 4.5 | |
| 0 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.4 |