Grade 20 Titanium vs. C77300 Nickel Silver
Grade 20 titanium belongs to the titanium alloys classification, while C77300 nickel silver belongs to the copper alloys. There are 19 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is grade 20 titanium and the bottom bar is C77300 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Poisson's Ratio | 0.32 | |
| 0.3 |
| Shear Modulus, GPa | 47 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 900 to 1270 | |
| 540 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 180 |
| Maximum Temperature: Mechanical, °C | 370 | |
| 130 |
| Melting Completion (Liquidus), °C | 1660 | |
| 940 |
| Melting Onset (Solidus), °C | 1600 | |
| 920 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 390 |
| Thermal Expansion, µm/m-K | 9.6 | |
| 20 |
Otherwise Unclassified Properties
| Density, g/cm3 | 5.0 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 52 | |
| 3.5 |
| Embodied Energy, MJ/kg | 860 | |
| 56 |
| Embodied Water, L/kg | 350 | |
| 310 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 7.7 |
| Stiffness to Weight: Bending, points | 33 | |
| 20 |
| Strength to Weight: Axial, points | 50 to 70 | |
| 19 |
| Strength to Weight: Bending, points | 41 to 52 | |
| 19 |
| Thermal Shock Resistance, points | 55 to 77 | |
| 17 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 3.0 to 4.0 | |
| 0 to 0.010 |
| Carbon (C), % | 0 to 0.050 | |
| 0 |
| Chromium (Cr), % | 5.5 to 6.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 46 to 50 |
| Hydrogen (H), % | 0 to 0.020 | |
| 0 |
| Iron (Fe), % | 0 to 0.3 | |
| 0 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Molybdenum (Mo), % | 3.5 to 4.5 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 9.0 to 11 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.12 | |
| 0 |
| Palladium (Pd), % | 0.040 to 0.080 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.25 |
| Silicon (Si), % | 0 | |
| 0.040 to 0.25 |
| Titanium (Ti), % | 71 to 77 | |
| 0 |
| Vanadium (V), % | 7.5 to 8.5 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 37.9 to 45 |
| Zirconium (Zr), % | 3.5 to 4.5 | |
| 0 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.5 |