Grade 200 Maraging Steel vs. C94100 Bronze
Grade 200 maraging steel belongs to the iron alloys classification, while C94100 bronze belongs to the copper alloys. There are 23 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is grade 200 maraging steel and the bottom bar is C94100 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 92 |
| Elongation at Break, % | 9.1 to 18 | |
| 7.8 |
| Poisson's Ratio | 0.3 | |
| 0.36 |
| Shear Modulus, GPa | 74 | |
| 34 |
| Tensile Strength: Ultimate (UTS), MPa | 970 to 1500 | |
| 190 |
| Tensile Strength: Yield (Proof), MPa | 690 to 1490 | |
| 130 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 160 |
| Melting Completion (Liquidus), °C | 1460 | |
| 870 |
| Melting Onset (Solidus), °C | 1420 | |
| 790 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 330 |
| Thermal Expansion, µm/m-K | 12 | |
| 20 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 29 |
| Density, g/cm3 | 8.2 | |
| 9.2 |
| Embodied Carbon, kg CO2/kg material | 4.5 | |
| 3.0 |
| Embodied Energy, MJ/kg | 59 | |
| 48 |
| Embodied Water, L/kg | 140 | |
| 370 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 to 160 | |
| 14 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1240 to 5740 | |
| 97 |
| Stiffness to Weight: Axial, points | 13 | |
| 5.5 |
| Stiffness to Weight: Bending, points | 23 | |
| 16 |
| Strength to Weight: Axial, points | 33 to 51 | |
| 5.8 |
| Strength to Weight: Bending, points | 27 to 35 | |
| 8.1 |
| Thermal Shock Resistance, points | 29 to 45 | |
| 7.6 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0.050 to 0.15 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 | |
| 0 to 0.8 |
| Boron (B), % | 0 to 0.0030 | |
| 0 |
| Calcium (Ca), % | 0 to 0.050 | |
| 0 |
| Carbon (C), % | 0 to 0.030 | |
| 0 |
| Cobalt (Co), % | 8.0 to 9.0 | |
| 0 |
| Copper (Cu), % | 0 | |
| 72 to 79 |
| Iron (Fe), % | 67.8 to 71.8 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 | |
| 18 to 22 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 |
| Molybdenum (Mo), % | 3.0 to 3.5 | |
| 0 |
| Nickel (Ni), % | 17 to 19 | |
| 0 to 1.0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 1.5 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.0050 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.080 |
| Tin (Sn), % | 0 | |
| 4.5 to 6.5 |
| Titanium (Ti), % | 0.15 to 0.25 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 1.0 |
| Zirconium (Zr), % | 0 to 0.020 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 1.3 |