Grade 21 Titanium vs. AWS ERTi-2

Both grade 21 titanium and AWS ERTi-2 are titanium alloys. They have 79% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is grade 21 titanium and the bottom bar is AWS ERTi-2.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 140
110
Elongation at Break, % 9.0 to 17
20
Fatigue Strength, MPa 550 to 660
190
Poisson's Ratio 0.32
0.32
Shear Modulus, GPa 51
40
Tensile Strength: Ultimate (UTS), MPa 890 to 1340
340
Tensile Strength: Yield (Proof), MPa 870 to 1170
280

Thermal Properties

Latent Heat of Fusion, J/g 410
420
Maximum Temperature: Mechanical, °C 310
320
Melting Completion (Liquidus), °C 1740
1670
Melting Onset (Solidus), °C 1690
1620
Specific Heat Capacity, J/kg-K 500
540
Thermal Conductivity, W/m-K 7.5
21
Thermal Expansion, µm/m-K 7.1
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 60
37
Density, g/cm3 5.4
4.5
Embodied Carbon, kg CO2/kg material 32
31
Embodied Energy, MJ/kg 490
510
Embodied Water, L/kg 180
110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 180
64
Resilience: Unit (Modulus of Resilience), kJ/m3 2760 to 5010
360
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 32
35
Strength to Weight: Axial, points 46 to 69
21
Strength to Weight: Bending, points 38 to 50
24
Thermal Diffusivity, mm2/s 2.8
8.7
Thermal Shock Resistance, points 66 to 100
27

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 2.5 to 3.5
0
Carbon (C), % 0 to 0.050
0 to 0.030
Hydrogen (H), % 0 to 0.015
0 to 0.0080
Iron (Fe), % 0 to 0.4
0 to 0.12
Molybdenum (Mo), % 14 to 16
0
Niobium (Nb), % 2.2 to 3.2
0
Nitrogen (N), % 0 to 0.030
0 to 0.015
Oxygen (O), % 0 to 0.17
0.080 to 0.16
Silicon (Si), % 0.15 to 0.25
0
Titanium (Ti), % 76 to 81.2
99.667 to 99.92
Residuals, % 0 to 0.4
0