Grade 250 Maraging Steel vs. 7049 Aluminum
Grade 250 maraging steel belongs to the iron alloys classification, while 7049 aluminum belongs to the aluminum alloys. There are 23 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is grade 250 maraging steel and the bottom bar is 7049 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 70 |
| Elongation at Break, % | 7.3 to 17 | |
| 6.2 to 7.0 |
| Poisson's Ratio | 0.3 | |
| 0.32 |
| Shear Modulus, GPa | 75 | |
| 27 |
| Shear Strength, MPa | 600 to 1060 | |
| 300 to 310 |
| Tensile Strength: Ultimate (UTS), MPa | 970 to 1800 | |
| 510 to 530 |
| Tensile Strength: Yield (Proof), MPa | 660 to 1740 | |
| 420 to 450 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 370 |
| Melting Completion (Liquidus), °C | 1480 | |
| 640 |
| Melting Onset (Solidus), °C | 1430 | |
| 480 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 860 |
| Thermal Expansion, µm/m-K | 12 | |
| 23 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 32 | |
| 10 |
| Density, g/cm3 | 8.2 | |
| 3.1 |
| Embodied Carbon, kg CO2/kg material | 4.9 | |
| 8.1 |
| Embodied Energy, MJ/kg | 65 | |
| 140 |
| Embodied Water, L/kg | 140 | |
| 1110 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 to 150 | |
| 31 to 34 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 45 |
| Strength to Weight: Axial, points | 33 to 61 | |
| 46 to 47 |
| Strength to Weight: Bending, points | 26 to 40 | |
| 46 to 47 |
| Thermal Shock Resistance, points | 29 to 54 | |
| 22 to 23 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0.050 to 0.15 | |
| 85.7 to 89.5 |
| Boron (B), % | 0 to 0.0030 | |
| 0 |
| Calcium (Ca), % | 0 to 0.050 | |
| 0 |
| Carbon (C), % | 0 to 0.030 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0.1 to 0.22 |
| Cobalt (Co), % | 7.0 to 8.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 1.2 to 1.9 |
| Iron (Fe), % | 66.3 to 71.1 | |
| 0 to 0.35 |
| Magnesium (Mg), % | 0 | |
| 2.0 to 2.9 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 to 0.2 |
| Molybdenum (Mo), % | 4.6 to 5.2 | |
| 0 |
| Nickel (Ni), % | 17 to 19 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.25 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 |
| Titanium (Ti), % | 0.3 to 0.5 | |
| 0 to 0.1 |
| Zinc (Zn), % | 0 | |
| 7.2 to 8.2 |
| Zirconium (Zr), % | 0 to 0.020 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.15 |