Grade 250 Maraging Steel vs. ASTM A387 Grade 11 Steel
Both grade 250 maraging steel and ASTM A387 grade 11 steel are iron alloys. They have 69% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is grade 250 maraging steel and the bottom bar is ASTM A387 grade 11 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 7.3 to 17 | |
| 25 |
| Poisson's Ratio | 0.3 | |
| 0.29 |
| Shear Modulus, GPa | 75 | |
| 73 |
| Shear Strength, MPa | 600 to 1060 | |
| 320 to 390 |
| Tensile Strength: Ultimate (UTS), MPa | 970 to 1800 | |
| 500 to 600 |
| Tensile Strength: Yield (Proof), MPa | 660 to 1740 | |
| 270 to 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 260 |
| Melting Completion (Liquidus), °C | 1480 | |
| 1460 |
| Melting Onset (Solidus), °C | 1430 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 32 | |
| 2.9 |
| Density, g/cm3 | 8.2 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 4.9 | |
| 1.6 |
| Embodied Energy, MJ/kg | 65 | |
| 21 |
| Embodied Water, L/kg | 140 | |
| 53 |
Common Calculations
| PREN (Pitting Resistance) | 16 | |
| 3.1 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 to 150 | |
| 100 to 130 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 33 to 61 | |
| 18 to 21 |
| Strength to Weight: Bending, points | 26 to 40 | |
| 18 to 20 |
| Thermal Shock Resistance, points | 29 to 54 | |
| 15 to 18 |
Alloy Composition
| Aluminum (Al), % | 0.050 to 0.15 | |
| 0 |
| Boron (B), % | 0 to 0.0030 | |
| 0 |
| Calcium (Ca), % | 0 to 0.050 | |
| 0 |
| Carbon (C), % | 0 to 0.030 | |
| 0.050 to 0.17 |
| Chromium (Cr), % | 0 | |
| 1.0 to 1.5 |
| Cobalt (Co), % | 7.0 to 8.5 | |
| 0 |
| Iron (Fe), % | 66.3 to 71.1 | |
| 96.2 to 97.6 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0.4 to 0.65 |
| Molybdenum (Mo), % | 4.6 to 5.2 | |
| 0.45 to 0.65 |
| Nickel (Ni), % | 17 to 19 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.1 | |
| 0.5 to 0.8 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.025 |
| Titanium (Ti), % | 0.3 to 0.5 | |
| 0 |
| Zirconium (Zr), % | 0 to 0.020 | |
| 0 |