Grade 250 Maraging Steel vs. ISO-WD32250 Magnesium
Grade 250 maraging steel belongs to the iron alloys classification, while ISO-WD32250 magnesium belongs to the magnesium alloys. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is grade 250 maraging steel and the bottom bar is ISO-WD32250 magnesium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 45 |
| Elongation at Break, % | 7.3 to 17 | |
| 4.5 to 8.6 |
| Poisson's Ratio | 0.3 | |
| 0.29 |
| Shear Modulus, GPa | 75 | |
| 17 |
| Shear Strength, MPa | 600 to 1060 | |
| 180 to 190 |
| Tensile Strength: Ultimate (UTS), MPa | 970 to 1800 | |
| 310 to 330 |
| Tensile Strength: Yield (Proof), MPa | 660 to 1740 | |
| 240 to 290 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 340 |
| Melting Completion (Liquidus), °C | 1480 | |
| 600 |
| Melting Onset (Solidus), °C | 1430 | |
| 550 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 980 |
| Thermal Expansion, µm/m-K | 12 | |
| 26 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 32 | |
| 13 |
| Density, g/cm3 | 8.2 | |
| 1.8 |
| Embodied Carbon, kg CO2/kg material | 4.9 | |
| 24 |
| Embodied Energy, MJ/kg | 65 | |
| 160 |
| Embodied Water, L/kg | 140 | |
| 950 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 to 150 | |
| 14 to 26 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 67 |
| Strength to Weight: Axial, points | 33 to 61 | |
| 49 to 51 |
| Strength to Weight: Bending, points | 26 to 40 | |
| 58 to 60 |
| Thermal Shock Resistance, points | 29 to 54 | |
| 19 to 20 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0.050 to 0.15 | |
| 0 |
| Boron (B), % | 0 to 0.0030 | |
| 0 |
| Calcium (Ca), % | 0 to 0.050 | |
| 0 |
| Carbon (C), % | 0 to 0.030 | |
| 0 |
| Cobalt (Co), % | 7.0 to 8.5 | |
| 0 |
| Iron (Fe), % | 66.3 to 71.1 | |
| 0 |
| Magnesium (Mg), % | 0 | |
| 94.9 to 97.1 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 |
| Molybdenum (Mo), % | 4.6 to 5.2 | |
| 0 |
| Nickel (Ni), % | 17 to 19 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 |
| Titanium (Ti), % | 0.3 to 0.5 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 2.5 to 4.0 |
| Zirconium (Zr), % | 0 to 0.020 | |
| 0.45 to 0.8 |
| Residuals, % | 0 | |
| 0 to 0.3 |