Grade 26 Titanium vs. Solder Alloy 716

Grade 26 titanium belongs to the titanium alloys classification, while solder alloy 716 belongs to the otherwise unclassified metals. There are 22 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is grade 26 titanium and the bottom bar is solder alloy 716.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
51
Elongation at Break, % 23
13
Poisson's Ratio 0.32
0.36
Shear Modulus, GPa 41
19
Tensile Strength: Ultimate (UTS), MPa 390
39

Thermal Properties

Latent Heat of Fusion, J/g 420
60
Melting Completion (Liquidus), °C 1660
230
Melting Onset (Solidus), °C 1610
220
Specific Heat Capacity, J/kg-K 540
220
Thermal Conductivity, W/m-K 21
60
Thermal Expansion, µm/m-K 9.2
22

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.4
13
Electrical Conductivity: Equal Weight (Specific), % IACS 6.9
16

Otherwise Unclassified Properties

Density, g/cm3 4.5
7.3
Embodied Carbon, kg CO2/kg material 33
16
Embodied Energy, MJ/kg 530
270

Common Calculations

Stiffness to Weight: Axial, points 13
3.8
Stiffness to Weight: Bending, points 35
17
Strength to Weight: Axial, points 24
1.5
Strength to Weight: Bending, points 26
3.5
Thermal Diffusivity, mm2/s 8.6
37
Thermal Shock Resistance, points 28
2.5

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.1
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0 to 0.080
0
Copper (Cu), % 0
0.3 to 0.7
Gold (Au), % 0
0 to 0.050
Hydrogen (H), % 0 to 0.015
0
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0 to 0.3
0 to 0.020
Lead (Pb), % 0
0 to 0.070
Nickel (Ni), % 0
0 to 0.010
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.25
0
Ruthenium (Ru), % 0.080 to 0.14
0
Silver (Ag), % 0
0.8 to 1.2
Tin (Sn), % 0
97.6 to 98.9
Titanium (Ti), % 98.8 to 99.92
0
Zinc (Zn), % 0
0 to 0.0010
Residuals, % 0 to 0.4
0