Grade 28 Titanium vs. AISI 440A Stainless Steel
Grade 28 titanium belongs to the titanium alloys classification, while AISI 440A stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is grade 28 titanium and the bottom bar is AISI 440A stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 200 |
| Elongation at Break, % | 11 to 17 | |
| 5.0 to 20 |
| Fatigue Strength, MPa | 330 to 480 | |
| 270 to 790 |
| Poisson's Ratio | 0.32 | |
| 0.28 |
| Shear Modulus, GPa | 40 | |
| 77 |
| Shear Strength, MPa | 420 to 590 | |
| 450 to 1040 |
| Tensile Strength: Ultimate (UTS), MPa | 690 to 980 | |
| 730 to 1790 |
| Tensile Strength: Yield (Proof), MPa | 540 to 810 | |
| 420 to 1650 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 330 | |
| 760 |
| Melting Completion (Liquidus), °C | 1640 | |
| 1480 |
| Melting Onset (Solidus), °C | 1590 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 550 | |
| 480 |
| Thermal Conductivity, W/m-K | 8.3 | |
| 23 |
| Thermal Expansion, µm/m-K | 9.9 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.3 | |
| 2.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 2.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 36 | |
| 9.0 |
| Density, g/cm3 | 4.5 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 37 | |
| 2.2 |
| Embodied Energy, MJ/kg | 600 | |
| 31 |
| Embodied Water, L/kg | 370 | |
| 120 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 87 to 110 | |
| 87 to 120 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 35 | |
| 25 |
| Strength to Weight: Axial, points | 43 to 61 | |
| 26 to 65 |
| Strength to Weight: Bending, points | 39 to 49 | |
| 23 to 43 |
| Thermal Diffusivity, mm2/s | 3.4 | |
| 6.2 |
| Thermal Shock Resistance, points | 47 to 66 | |
| 26 to 65 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 2.5 to 3.5 | |
| 0 |
| Carbon (C), % | 0 to 0.080 | |
| 0.6 to 0.75 |
| Chromium (Cr), % | 0 | |
| 16 to 18 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.25 | |
| 78.4 to 83.4 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.75 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.15 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Ruthenium (Ru), % | 0.080 to 0.14 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Titanium (Ti), % | 92.4 to 95.4 | |
| 0 |
| Vanadium (V), % | 2.0 to 3.0 | |
| 0 |
| Residuals, % | 0 to 0.4 | |
| 0 |