Grade 28 Titanium vs. AWS E80C-B6
Grade 28 titanium belongs to the titanium alloys classification, while AWS E80C-B6 belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is grade 28 titanium and the bottom bar is AWS E80C-B6.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Elongation at Break, % | 11 to 17 | |
| 19 |
| Poisson's Ratio | 0.32 | |
| 0.29 |
| Shear Modulus, GPa | 40 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 690 to 980 | |
| 630 |
| Tensile Strength: Yield (Proof), MPa | 540 to 810 | |
| 530 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 260 |
| Melting Completion (Liquidus), °C | 1640 | |
| 1450 |
| Melting Onset (Solidus), °C | 1590 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 550 | |
| 470 |
| Thermal Conductivity, W/m-K | 8.3 | |
| 39 |
| Thermal Expansion, µm/m-K | 9.9 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.3 | |
| 8.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 9.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 36 | |
| 4.7 |
| Density, g/cm3 | 4.5 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 37 | |
| 1.8 |
| Embodied Energy, MJ/kg | 600 | |
| 25 |
| Embodied Water, L/kg | 370 | |
| 71 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 87 to 110 | |
| 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1370 to 3100 | |
| 730 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 35 | |
| 25 |
| Strength to Weight: Axial, points | 43 to 61 | |
| 22 |
| Strength to Weight: Bending, points | 39 to 49 | |
| 21 |
| Thermal Diffusivity, mm2/s | 3.4 | |
| 11 |
| Thermal Shock Resistance, points | 47 to 66 | |
| 18 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 2.5 to 3.5 | |
| 0 |
| Carbon (C), % | 0 to 0.080 | |
| 0 to 0.1 |
| Chromium (Cr), % | 0 | |
| 4.5 to 6.0 |
| Copper (Cu), % | 0 | |
| 0 to 0.35 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.25 | |
| 90.1 to 94.4 |
| Manganese (Mn), % | 0 | |
| 0.4 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 0.45 to 0.65 |
| Nickel (Ni), % | 0 | |
| 0 to 0.6 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.15 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Ruthenium (Ru), % | 0.080 to 0.14 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0.25 to 0.6 |
| Sulfur (S), % | 0 | |
| 0 to 0.025 |
| Titanium (Ti), % | 92.4 to 95.4 | |
| 0 |
| Vanadium (V), % | 2.0 to 3.0 | |
| 0 to 0.030 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.5 |