Grade 28 Titanium vs. N07041 Nickel

Grade 28 titanium belongs to the titanium alloys classification, while N07041 nickel belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is grade 28 titanium and the bottom bar is N07041 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
220
Elongation at Break, % 11 to 17
14
Fatigue Strength, MPa 330 to 480
540
Shear Strength, MPa 420 to 590
850
Tensile Strength: Ultimate (UTS), MPa 690 to 980
1400
Tensile Strength: Yield (Proof), MPa 540 to 810
1050

Thermal Properties

Melting Onset (Solidus), °C 1590
1320
Specific Heat Capacity, J/kg-K 550
450
Thermal Conductivity, W/m-K 8.3
11
Thermal Expansion, µm/m-K 9.9
12

Otherwise Unclassified Properties

Density, g/cm3 4.5
8.2

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 87 to 110
180
Resilience: Unit (Modulus of Resilience), kJ/m3 1370 to 3100
2510
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 35
25
Strength to Weight: Axial, points 43 to 61
47
Strength to Weight: Bending, points 39 to 49
34
Thermal Diffusivity, mm2/s 3.4
3.0
Thermal Shock Resistance, points 47 to 66
38