Grade 29 Titanium vs. R60705 Alloy
Grade 29 titanium belongs to the titanium alloys classification, while R60705 alloy belongs to the otherwise unclassified metals. There are 21 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is grade 29 titanium and the bottom bar is R60705 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 98 |
| Elongation at Break, % | 6.8 to 11 | |
| 18 |
| Fatigue Strength, MPa | 460 to 510 | |
| 290 |
| Poisson's Ratio | 0.32 | |
| 0.34 |
| Shear Modulus, GPa | 40 | |
| 37 |
| Tensile Strength: Ultimate (UTS), MPa | 930 to 940 | |
| 540 |
| Tensile Strength: Yield (Proof), MPa | 850 to 870 | |
| 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 560 | |
| 270 |
| Thermal Conductivity, W/m-K | 7.3 | |
| 17 |
| Thermal Expansion, µm/m-K | 9.3 | |
| 6.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 4.5 | |
| 6.7 |
| Embodied Water, L/kg | 410 | |
| 450 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 62 to 100 | |
| 90 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 3420 to 3540 | |
| 950 |
| Stiffness to Weight: Axial, points | 13 | |
| 8.1 |
| Stiffness to Weight: Bending, points | 35 | |
| 23 |
| Strength to Weight: Axial, points | 58 to 59 | |
| 22 |
| Strength to Weight: Bending, points | 47 to 48 | |
| 22 |
| Thermal Diffusivity, mm2/s | 2.9 | |
| 9.5 |
| Thermal Shock Resistance, points | 68 to 69 | |
| 63 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 5.5 to 6.5 | |
| 0 |
| Carbon (C), % | 0 to 0.080 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0 | |
| 0 to 0.2 |
| Hafnium (Hf), % | 0 | |
| 0 to 4.5 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 to 0.0050 |
| Iron (Fe), % | 0 to 0.25 | |
| 0 to 0.2 |
| Niobium (Nb), % | 0 | |
| 2.0 to 3.0 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 to 0.025 |
| Oxygen (O), % | 0 to 0.13 | |
| 0 to 0.18 |
| Ruthenium (Ru), % | 0.080 to 0.14 | |
| 0 |
| Titanium (Ti), % | 88 to 90.9 | |
| 0 |
| Vanadium (V), % | 3.5 to 4.5 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 91 to 98 |
| Residuals, % | 0 to 0.4 | |
| 0 |