Grade 3 Babbitt Metal vs. ACI-ASTM CF3M Steel
Grade 3 Babbitt Metal belongs to the otherwise unclassified metals classification, while ACI-ASTM CF3M steel belongs to the iron alloys. There are 18 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is grade 3 Babbitt Metal and the bottom bar is ACI-ASTM CF3M steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 27 | |
| 150 |
| Elastic (Young's, Tensile) Modulus, GPa | 56 | |
| 200 |
| Poisson's Ratio | 0.35 | |
| 0.28 |
| Shear Modulus, GPa | 21 | |
| 78 |
| Tensile Strength: Yield (Proof), MPa | 46 | |
| 260 |
Thermal Properties
| Latent Heat of Fusion, J/g | 79 | |
| 300 |
| Melting Completion (Liquidus), °C | 420 | |
| 1440 |
| Melting Onset (Solidus), °C | 240 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 230 | |
| 470 |
| Thermal Expansion, µm/m-K | 21 | |
| 15 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 70 | |
| 19 |
| Density, g/cm3 | 7.4 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 12 | |
| 3.8 |
| Embodied Energy, MJ/kg | 200 | |
| 53 |
| Embodied Water, L/kg | 1210 | |
| 160 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 19 | |
| 170 |
| Stiffness to Weight: Axial, points | 4.2 | |
| 14 |
| Stiffness to Weight: Bending, points | 17 | |
| 25 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0050 | |
| 0 |
| Antimony (Sb), % | 7.5 to 8.5 | |
| 0 |
| Arsenic (As), % | 0 to 0.1 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.080 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.050 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0 | |
| 17 to 21 |
| Copper (Cu), % | 7.5 to 8.5 | |
| 0 |
| Iron (Fe), % | 0 to 0.080 | |
| 59.9 to 72 |
| Lead (Pb), % | 0 to 0.35 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0 | |
| 2.0 to 3.0 |
| Nickel (Ni), % | 0 | |
| 9.0 to 13 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 0 to 1.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.040 |
| Tin (Sn), % | 82.3 to 85 | |
| 0 |
| Zinc (Zn), % | 0 to 0.0050 | |
| 0 |