Grade 3 Babbitt Metal vs. AWS BAg-1a

Both grade 3 Babbitt Metal and AWS BAg-1a are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 13 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is grade 3 Babbitt Metal and the bottom bar is AWS BAg-1a.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 56
77
Poisson's Ratio 0.35
0.33
Shear Modulus, GPa 21
29

Thermal Properties

Latent Heat of Fusion, J/g 79
120
Melting Completion (Liquidus), °C 420
640
Melting Onset (Solidus), °C 240
630
Specific Heat Capacity, J/kg-K 230
280
Thermal Expansion, µm/m-K 21
22

Otherwise Unclassified Properties

Density, g/cm3 7.4
9.3
Embodied Carbon, kg CO2/kg material 12
48
Embodied Energy, MJ/kg 200
760

Common Calculations

Stiffness to Weight: Axial, points 4.2
4.6
Stiffness to Weight: Bending, points 17
15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.0050
0
Antimony (Sb), % 7.5 to 8.5
0
Arsenic (As), % 0 to 0.1
0
Bismuth (Bi), % 0 to 0.080
0
Cadmium (Cd), % 0 to 0.050
17 to 19
Copper (Cu), % 7.5 to 8.5
14.5 to 16.5
Iron (Fe), % 0 to 0.080
0
Lead (Pb), % 0 to 0.35
0
Silver (Ag), % 0
49 to 51
Tin (Sn), % 82.3 to 85
0
Zinc (Zn), % 0 to 0.0050
14.5 to 18.5
Residuals, % 0
0 to 0.15