Grade 3 Babbitt Metal vs. AWS BAg-9

Both grade 3 Babbitt Metal and AWS BAg-9 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 12 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is grade 3 Babbitt Metal and the bottom bar is AWS BAg-9.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 56
82
Poisson's Ratio 0.35
0.35
Shear Modulus, GPa 21
31

Thermal Properties

Latent Heat of Fusion, J/g 79
130
Melting Completion (Liquidus), °C 420
720
Melting Onset (Solidus), °C 240
670
Specific Heat Capacity, J/kg-K 230
290
Thermal Expansion, µm/m-K 21
20

Otherwise Unclassified Properties

Density, g/cm3 7.4
9.6
Embodied Energy, MJ/kg 200
980

Common Calculations

Stiffness to Weight: Axial, points 4.2
4.8
Stiffness to Weight: Bending, points 17
15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.0050
0
Antimony (Sb), % 7.5 to 8.5
0
Arsenic (As), % 0 to 0.1
0
Bismuth (Bi), % 0 to 0.080
0
Cadmium (Cd), % 0 to 0.050
0
Copper (Cu), % 7.5 to 8.5
19 to 21
Iron (Fe), % 0 to 0.080
0
Lead (Pb), % 0 to 0.35
0
Silver (Ag), % 0
64 to 66
Tin (Sn), % 82.3 to 85
0
Zinc (Zn), % 0 to 0.0050
13 to 17
Residuals, % 0
0 to 0.15