Grade 3 Babbitt Metal vs. Grade 363 Molybdenum

Both grade 3 Babbitt Metal and grade 363 molybdenum are otherwise unclassified metals. There are 14 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is grade 3 Babbitt Metal and the bottom bar is grade 363 molybdenum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 56
310
Poisson's Ratio 0.35
0.31
Shear Modulus, GPa 21
120
Tensile Strength: Yield (Proof), MPa 46
350 to 620

Thermal Properties

Latent Heat of Fusion, J/g 79
370
Specific Heat Capacity, J/kg-K 230
250
Thermal Expansion, µm/m-K 21
7.0

Otherwise Unclassified Properties

Density, g/cm3 7.4
10
Embodied Carbon, kg CO2/kg material 12
28
Embodied Energy, MJ/kg 200
330
Embodied Water, L/kg 1210
360

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 19
200 to 630
Stiffness to Weight: Axial, points 4.2
17
Stiffness to Weight: Bending, points 17
22

Alloy Composition

Aluminum (Al), % 0 to 0.0050
0
Antimony (Sb), % 7.5 to 8.5
0
Arsenic (As), % 0 to 0.1
0
Bismuth (Bi), % 0 to 0.080
0
Cadmium (Cd), % 0 to 0.050
0
Carbon (C), % 0
0.010 to 0.030
Copper (Cu), % 7.5 to 8.5
0
Iron (Fe), % 0 to 0.080
0 to 0.010
Lead (Pb), % 0 to 0.35
0
Molybdenum (Mo), % 0
99.3 to 99.5
Nickel (Ni), % 0
0 to 0.0020
Nitrogen (N), % 0
0 to 0.0020
Oxygen (O), % 0
0 to 0.0030
Silicon (Si), % 0
0 to 0.010
Tin (Sn), % 82.3 to 85
0
Titanium (Ti), % 0
0.4 to 0.55
Zinc (Zn), % 0 to 0.0050
0
Zirconium (Zr), % 0
0.060 to 0.12