Grade 3 Babbitt Metal vs. SAE-AISI H13 Steel

Grade 3 Babbitt Metal belongs to the otherwise unclassified metals classification, while SAE-AISI H13 steel belongs to the iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is grade 3 Babbitt Metal and the bottom bar is SAE-AISI H13 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 56
190
Poisson's Ratio 0.35
0.29
Shear Modulus, GPa 21
74

Thermal Properties

Latent Heat of Fusion, J/g 79
270
Melting Completion (Liquidus), °C 420
1460
Melting Onset (Solidus), °C 240
1420
Specific Heat Capacity, J/kg-K 230
470
Thermal Expansion, µm/m-K 21
10

Otherwise Unclassified Properties

Base Metal Price, % relative 70
6.0
Density, g/cm3 7.4
7.8
Embodied Carbon, kg CO2/kg material 12
4.3
Embodied Energy, MJ/kg 200
64
Embodied Water, L/kg 1210
78

Common Calculations

Stiffness to Weight: Axial, points 4.2
14
Stiffness to Weight: Bending, points 17
25

Alloy Composition

Aluminum (Al), % 0 to 0.0050
0
Antimony (Sb), % 7.5 to 8.5
0
Arsenic (As), % 0 to 0.1
0
Bismuth (Bi), % 0 to 0.080
0
Cadmium (Cd), % 0 to 0.050
0
Carbon (C), % 0
0.32 to 0.45
Chromium (Cr), % 0
4.8 to 5.5
Copper (Cu), % 7.5 to 8.5
0 to 0.25
Iron (Fe), % 0 to 0.080
88.8 to 92
Lead (Pb), % 0 to 0.35
0
Manganese (Mn), % 0
0.2 to 0.5
Molybdenum (Mo), % 0
1.1 to 1.8
Nickel (Ni), % 0
0 to 0.3
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0.8 to 1.2
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 82.3 to 85
0
Vanadium (V), % 0
0.8 to 1.2
Zinc (Zn), % 0 to 0.0050
0