Grade 3 Babbitt Metal vs. C66200 Brass

Grade 3 Babbitt Metal belongs to the otherwise unclassified metals classification, while C66200 brass belongs to the copper alloys. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is grade 3 Babbitt Metal and the bottom bar is C66200 brass.

Grade 3 (L13840) Tin-Base Babbitt Metal UNS C66200 Nickel Brass

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		56
Elastic (Young's, Tensile) Modulus, GPa		110

Poisson's Ratio		0.35
Poisson's Ratio		0.33

Shear Modulus, GPa		21
Shear Modulus, GPa		42

Tensile Strength: Yield (Proof), MPa		46
Tensile Strength: Yield (Proof), MPa		410 to 480

Thermal Properties

Latent Heat of Fusion, J/g		79
Latent Heat of Fusion, J/g		200

Melting Completion (Liquidus), °C		420
Melting Completion (Liquidus), °C		1070

Melting Onset (Solidus), °C		240
Melting Onset (Solidus), °C		1030

Specific Heat Capacity, J/kg-K		230
Specific Heat Capacity, J/kg-K		390

Thermal Expansion, µm/m-K		21
Thermal Expansion, µm/m-K		18

Otherwise Unclassified Properties

Base Metal Price, % relative		70
Base Metal Price, % relative		29

Density, g/cm³		7.4
Density, g/cm³		8.7

Embodied Carbon, kg CO₂/kg material		12
Embodied Carbon, kg CO₂/kg material		2.7

Embodied Energy, MJ/kg		200
Embodied Energy, MJ/kg		43

Embodied Water, L/kg		1210
Embodied Water, L/kg		320

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m³		19
Resilience: Unit (Modulus of Resilience), kJ/m³		760 to 1030

Stiffness to Weight: Axial, points		4.2
Stiffness to Weight: Axial, points		7.2

Stiffness to Weight: Bending, points		17
Stiffness to Weight: Bending, points		19

Alloy Composition

Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460

Aluminum (Al), %		0 to 0.0050
Aluminum (Al), %		0

Antimony (Sb), %		7.5 to 8.5
Antimony (Sb), %		0

Arsenic (As), %		0 to 0.1
Arsenic (As), %		0

Bismuth (Bi), %		0 to 0.080
Bismuth (Bi), %		0

Cadmium (Cd), %		0 to 0.050
Cadmium (Cd), %		0

Copper (Cu), %		7.5 to 8.5
Copper (Cu), %		86.6 to 91

Iron (Fe), %		0 to 0.080
Iron (Fe), %		0 to 0.050

Lead (Pb), %		0 to 0.35
Lead (Pb), %		0 to 0.050

Nickel (Ni), %		0
Nickel (Ni), %		0.3 to 1.0

Phosphorus (P), %		0
Phosphorus (P), %		0.050 to 0.2

Tin (Sn), %		82.3 to 85
Tin (Sn), %		0.2 to 0.7

Zinc (Zn), %		0 to 0.0050
Zinc (Zn), %		6.5 to 12.9

Residuals, %		0
Residuals, %		0 to 0.5