Grade 3 Babbitt Metal vs. K93600 Alloy
Grade 3 Babbitt Metal belongs to the otherwise unclassified metals classification, while K93600 alloy belongs to the iron alloys. There are 9 material properties with values for both materials. Properties with values for just one material (23, in this case) are not shown.
For each property being compared, the top bar is grade 3 Babbitt Metal and the bottom bar is K93600 alloy.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 7.4 | |
| 8.1 |
| Elastic (Young's, Tensile) Modulus, GPa | 56 | |
| 140 |
| Melting Onset (Solidus), °C | 240 | |
| 1430 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 19 | |
| 280 to 2050 |
| Specific Heat Capacity, J/kg-K | 230 | |
| 520 |
| Stiffness to Weight: Axial, points | 4.2 | |
| 9.4 |
| Stiffness to Weight: Bending, points | 17 | |
| 21 |
| Tensile Strength: Yield (Proof), MPa | 46 | |
| 280 to 750 |
| Thermal Expansion, µm/m-K | 21 | |
| 7.3 |