Grade 3 Babbitt Metal vs. R60706 Alloy

Both grade 3 Babbitt Metal and R60706 alloy are otherwise unclassified metals. There are 12 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is grade 3 Babbitt Metal and the bottom bar is R60706 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 56
98
Poisson's Ratio 0.35
0.34
Shear Modulus, GPa 21
37
Tensile Strength: Yield (Proof), MPa 46
390

Thermal Properties

Latent Heat of Fusion, J/g 79
250
Specific Heat Capacity, J/kg-K 230
270
Thermal Expansion, µm/m-K 21
6.3

Otherwise Unclassified Properties

Density, g/cm3 7.4
6.7
Embodied Water, L/kg 1210
450

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 19
760
Stiffness to Weight: Axial, points 4.2
8.1
Stiffness to Weight: Bending, points 17
23

Alloy Composition

Aluminum (Al), % 0 to 0.0050
0
Antimony (Sb), % 7.5 to 8.5
0
Arsenic (As), % 0 to 0.1
0
Bismuth (Bi), % 0 to 0.080
0
Cadmium (Cd), % 0 to 0.050
0
Carbon (C), % 0
0 to 0.050
Chromium (Cr), % 0
0 to 0.2
Copper (Cu), % 7.5 to 8.5
0
Hafnium (Hf), % 0
0 to 4.5
Hydrogen (H), % 0
0 to 0.0050
Iron (Fe), % 0 to 0.080
0 to 0.2
Lead (Pb), % 0 to 0.35
0
Niobium (Nb), % 0
2.0 to 3.0
Nitrogen (N), % 0
0 to 0.025
Oxygen (O), % 0
0 to 0.16
Tin (Sn), % 82.3 to 85
0
Zinc (Zn), % 0 to 0.0050
0
Zirconium (Zr), % 0
91 to 98