Grade 3 Babbitt Metal vs. Z41121 Zinc

Grade 3 Babbitt Metal belongs to the otherwise unclassified metals classification, while Z41121 zinc belongs to the zinc alloys. There are 17 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is grade 3 Babbitt Metal and the bottom bar is Z41121 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 56
87
Poisson's Ratio 0.35
0.25
Shear Modulus, GPa 21
35
Tensile Strength: Yield (Proof), MPa 46
120

Thermal Properties

Latent Heat of Fusion, J/g 79
110
Melting Completion (Liquidus), °C 420
410
Melting Onset (Solidus), °C 240
400
Specific Heat Capacity, J/kg-K 230
390
Thermal Expansion, µm/m-K 21
26

Otherwise Unclassified Properties

Base Metal Price, % relative 70
11
Density, g/cm3 7.4
6.6
Embodied Carbon, kg CO2/kg material 12
2.8
Embodied Energy, MJ/kg 200
54
Embodied Water, L/kg 1210
340

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 19
79
Stiffness to Weight: Axial, points 4.2
7.4
Stiffness to Weight: Bending, points 17
23

Alloy Composition

Aluminum (Al), % 0 to 0.0050
0 to 0.010
Antimony (Sb), % 7.5 to 8.5
0
Arsenic (As), % 0 to 0.1
0
Bismuth (Bi), % 0 to 0.080
0
Cadmium (Cd), % 0 to 0.050
0 to 0.0050
Copper (Cu), % 7.5 to 8.5
0.080 to 0.49
Iron (Fe), % 0 to 0.080
0 to 0.010
Lead (Pb), % 0 to 0.35
0 to 0.010
Tin (Sn), % 82.3 to 85
0 to 0.0030
Titanium (Ti), % 0
0.050 to 0.18
Zinc (Zn), % 0 to 0.0050
99.292 to 99.87