Grade 300 Maraging Steel vs. K1A Magnesium
Grade 300 maraging steel belongs to the iron alloys classification, while K1A magnesium belongs to the magnesium alloys. There are 23 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is grade 300 maraging steel and the bottom bar is K1A magnesium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 43 |
| Elongation at Break, % | 6.5 to 18 | |
| 13 |
| Poisson's Ratio | 0.3 | |
| 0.29 |
| Shear Modulus, GPa | 75 | |
| 17 |
| Shear Strength, MPa | 640 to 1190 | |
| 55 |
| Tensile Strength: Ultimate (UTS), MPa | 1030 to 2030 | |
| 180 |
| Tensile Strength: Yield (Proof), MPa | 760 to 1990 | |
| 51 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 350 |
| Melting Completion (Liquidus), °C | 1480 | |
| 650 |
| Melting Onset (Solidus), °C | 1430 | |
| 650 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 1000 |
| Thermal Expansion, µm/m-K | 12 | |
| 27 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 34 | |
| 13 |
| Density, g/cm3 | 8.2 | |
| 1.6 |
| Embodied Carbon, kg CO2/kg material | 5.1 | |
| 24 |
| Embodied Energy, MJ/kg | 68 | |
| 170 |
| Embodied Water, L/kg | 150 | |
| 970 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 to 170 | |
| 17 |
| Stiffness to Weight: Axial, points | 13 | |
| 15 |
| Stiffness to Weight: Bending, points | 23 | |
| 73 |
| Strength to Weight: Axial, points | 35 to 68 | |
| 31 |
| Strength to Weight: Bending, points | 28 to 43 | |
| 43 |
| Thermal Shock Resistance, points | 31 to 62 | |
| 11 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0.050 to 0.15 | |
| 0 |
| Boron (B), % | 0 to 0.0030 | |
| 0 |
| Calcium (Ca), % | 0 to 0.050 | |
| 0 |
| Carbon (C), % | 0 to 0.030 | |
| 0 |
| Cobalt (Co), % | 8.5 to 9.5 | |
| 0 |
| Iron (Fe), % | 65 to 68.4 | |
| 0 |
| Magnesium (Mg), % | 0 | |
| 98.7 to 99.6 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 |
| Molybdenum (Mo), % | 4.6 to 5.2 | |
| 0 |
| Nickel (Ni), % | 18 to 19 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 |
| Titanium (Ti), % | 0.5 to 0.8 | |
| 0 |
| Zirconium (Zr), % | 0 to 0.020 | |
| 0.4 to 1.0 |
| Residuals, % | 0 | |
| 0 to 0.3 |